New test method for mechanical strength evaluation of solar cell solder joints

2011年9月6日

By: R. Klengel*, R. Härtel*, S. Schindler**, D. Schade***, B. Sykes***

Motivation

Fraunhofer IWM, Fraunhofer CSP
Fraunhofer IWM, Fraunhofer CSP

A standardized method with clearly defined good-bad-criteria is not available for testing solder joints that connect single cells into strings. Thus, a comparative characterization of different manufacturers, cell types, base- and joining materials or joining technologies is impossible. The most commonly used test for solar cell ribbon interconnects is the pull test, as used in micro-electronics. For thin, brittle, large area silicon solar cells substantial modifications of the test equipment and methodology are required to realize a suitable metrology. In addition the factors influencing the defect conditions in multi crystalline material, high strains around the solder connect and inhomogeneous contact interfaces has to be considered.

New test method

Requirements to the test method:

  • reproducible (stabile test conditions, no silicon tears, …)
  • comparable (manufacturer, cell types, base- and joining materials, joining technology, …)
  • easy to handle (less handle steps, semi-automatic, little operator influences)
  • high throughput (little setting-up time, high test speed)
  • simply analyzable (statistics, visualization of test values and failure interface)
  • possible correlation to micro structure of solder joints

A XYZTEC Condor 250 multifunctional test machine was upgraded with a new designed test setup. The machine includes a vertical moving z-axis equipped with a force sensor and a x-y-stage for horizontal movement of the work holder. The X-Y table moves the cell at the same velocity than the z-axis pulls the solder ribbon. Thus the point of breakage remains under the measuring head and the test range equates to the ribbon length.

Measurement results XYZTEC Condor 250-3 Solar
Measurement results

Results

The graphical analysis of the measurement results and the images of the fracture interface allow correlating the pull force values with the corresponding failure mode. Every single change in the fracture interface is reproducible in the progression of the curve. So it seems to be possible to conclude to the solder joint condition by interpreting the measured curve.

SAM image of solder joint
SAM image of solder joint
X-ray image of solder joint
X-ray image of solder joint
Cross section of solder joint
Cross section of solder joint
Interface after pull test
Interface after pull test

To correlate the pull test measurement curves and fracture interfaces with concrete interface weakening like voids, non-wetted areas or microcracks etcetera different non-destructive analyzes of soldered bus bar interconnects like scanning acoustic microscopy (SAM) or X-ray inspection with following validation by metallographic cross sections were performed before the pull test.

Summary

With the developed test equipment and measurement routine it is succeeded to provide a reproducible, fast and easy handable method which is usable independent from solar cell geometry, condition of contact materials, soldering technology or manufacturer. It is possible to correlate the measurement curve of the pull test with the fracture interface. This allows to interpret the results with statements in terms of the solder joint quality.


*Fraunhofer Institute for Mechanics of Materials IWM, Walter-Huelse-Strasse 1, 06120 Halle (Saale), Germany Phone +49 (0) 345/5589-159,
** Fraunhofer Center for Silicon Photovoltaics CSP, Walter-Huelse-Strasse 1, 06120 Halle (Saale), Germany
***XYZTEC b.v., J.F.Kennedylaan 14-B, 5981 XC Panningen, The Netherlands

Download as PDF

Click here to download the complete "Mechanical Strength Evaluation of Solar Cell Solder Joints by Developing a New Test Method" as PDF.

Acknowledgement

This work was partly supported by the German Ministry of Economics and Technology under contract “ATSOLOT” (FKZ01FS10010).


最新的技術摘要

2019年7月 Meet the world’s biggest bond testers
2019年4月 Free SMTconnect ticket? Register now
2018年8月 Is Fully Automatic Bond Testing Possible?
2017年7月 Advances in Thin, 3D and MEMS Die Bond Strength Testing
2017年5月 Shear testing copper pillar
2017年3月 Fracture strength of thin wafers and die
2017年2月 Centralized database for enhanced security and SPC options
2017年1月 Full Automation with Improved Pattern Recognition, Fiducial Marks Analysis, Wire Detect and Failure Mode Analysis
2016年12月 Coating and film testing
2016年11月 Latest software release enables automatic grading
2016年10月 Vision enhanced materials testing
2016年9月 XYZTEC makes lid pull easy

 
Click to subscribe.

Other news

XYZTEC Newsletter

訂閱XYZTEC 最新的技術摘要

你的大名:

電子郵件地址:


© 1999-2016 XYZTEC BV Disclaimer, Privacy, Cookies
Technology leader in bond testing worldwide